Sticking for the principle of "Super Quality, Satisfactory service" ,We have been striving for being a superb small business partner of you for Digital Hardness Meter, V2 Block Calibration, Multi Purpose Welding Gauge, Special emphasis around the packaging of merchandise to avoid any damage during transportation,Detailed interest into the useful feedback and strategies of our esteemed shoppers.

Leading Manufacturer for Best Portable Hardness Tester – The Impact Device of Hardness Tester – TMTeck Detail:

The Impact Device of Hardness Tester

eutr (1) eutr (2)

Different Types of Impact Device

Material	Hardness method	Impact device
Material	Hardness method	D/DC	D+15	C	G	E	DL
Steel and cast steel	HRC	17.9～68.5	19.3～67.9	20.0～69.5		22.4～70.7	20.6～68.2
	HRB	59.6～99.6			47.7～99.9		37.0～99.9
	HRA	59.1~85.8				61.7～88.0
	HB	127～651	80～638	80～683	90～646	83～663	81～646
	HV	83～976	80～937	80～996		84～1042	80～950
	HS	32.2～99.5	33.3～99.3	31.8～102.1		35.8～102.6	30.6～96.8
Hammered steel	HB	143~650
Cold work tool steel	HRC	20.4～67.1	19.8～68.2	20.7～68.2		22.6～70.2
Cold work tool steel	HV	80～898	80～935	100～941		82～1009
Stainless steel	HRB	46.5～101.7
	HB	85～655
	HV	85～802
Gray cast iron	HRC
	HB	93～334			92～326
	HV
Nodular cast iron	HRC
	HB	131～387			127～364
	HV
Cast aluminum alloys	HB	19～164		23～210	32～168
Cast aluminum alloys	HRB	23.8～84.6		22.7～85.0	23.8～85.5
Brass(copper-zinc alloys)	HB	40～173
Brass(copper-zinc alloys)	HRB	13.5～95.3
Bronze (copper-aluminum/copper-tin alloys)	HB	60～290
Wrought copper alloys	HB	45～315

Non conventional impact devices		DC(D)/DL	D+15	C	G	E
Impacting energy Mass of impact body		11Mj 5.5g/7.2g	11mJ 7.8g	2.7mJ 3.0g	90mJ 20.0g	11mJ 5.5g
Test tip Hardness Diameter of test tip Material of test tip		1600HV 3mm Tungsten carbide	1600HV 3mm Tungsten carbide	1600HV 3mm Tungsten carbide	1600HV 5mm Tungsten carbide	5000HV 3mm synthetic diamond
Impact device Diameter Impact device Length Impact device Weight		20mm 86(147)/ 75mm 50g	20mm 162mm 80g	20mm 141mm 75g	30mm 254mm 250g	20mm 155mm 80g
Max. hardness of workpiece		940HV	940HV	1000HV	650HB	1200HV
Mean roughness of workpiece surface of the Ra		1.6μm	1.6μm	0.4μm	6.3μm	1.6μm
Min. weight of sample Measure directly Need support firmly Need coupling tightly		>5kg 2～5kg 0.05～2kg	>5kg 2～5kg 0.05～2kg	>1.5kg 0.5～1.5kg 0.02～0.5kg	>15kg 5～15kg 0.5～5kg	>5kg 2～5kg 0.05～2kg
Min. thickness of sample coupling tightly Min.layer thickness for surface harden		5mm ≥0.8mm	5mm ≥0.8mm	1mm ≥0.2mm	10mm ≥1.2mm	5mm ≥0.8mm
Size of tip indentation
Hardness 300HV	Indentation diameter	0.54mm	0.54mm	0.38mm	1.03mm	0.54mm
Hardness 300HV	Indentation depth	24μm	24μm	12μm	53μm	24μm
Hardness 600HV	Indentation diameter	0.54mm	0.54mm	0.32mm	0.90mm	0.54mm
Hardness 600HV	Indentation depth	17μm	17μm	8μm	41μm	17μm
Hardness 800HV	Indentation diameter	0.35mm	0.35mm	0.35mm	–	0.35mm
Hardness 800HV	Indentation depth	10μm	10μm	7μm	–	10μm
Available type of impact device		D: General test DC: Hole or hollow-cylindrical test DL: Slender narrow groove or hole test	D+15: groove or reentrant surface	C: small, light, thin parts or surface of hardend layer	G: large, thick, heavy or rough surface steel	E: super high hardness material

Type of Impact Device	Distance of center of the two indentations	Distance of center of the indentation to sample edge
Type of Impact Device	Not less than (mm)	Not less than (mm)
D、DC	3	5
DL	3	5
D+15	3	5
G	4	8
E	3	5
C	2	4

Product detail pictures:

Related Product Guide:

We have many excellent staff members good at marketing, QC, and dealing with kinds of troublesome problem in the production process for Leading Manufacturer for Best Portable Hardness Tester – The Impact Device of Hardness Tester – TMTeck , The product will supply to all over the world, such as: Amman, Romania, Serbia, If you need any of our products, or have other items to be produced, please send us your inquiries, samples or detailed drawings. Meanwhile, aiming to develop into an international enterprise group, we look forward to receiving offers for joint ventures and other cooperative projects.