OEM/ODM Factory Dynamic Hardness Tester - The Impact Device of Hardness Tester – TMTeck
OEM/ODM Factory Dynamic Hardness Tester - The Impact Device of Hardness Tester – TMTeck Detail:
The Impact Device of Hardness Tester
Different Types of Impact Device
Material |
Hardness method |
Impact device |
|||||
D/DC |
D+15 |
C |
G |
E |
DL |
||
Steel and cast steel |
HRC |
17.9~68.5 |
19.3~67.9 |
20.0~69.5 |
22.4~70.7 |
20.6~68.2 |
|
HRB |
59.6~99.6 |
47.7~99.9 |
37.0~99.9 |
||||
HRA |
59.1~85.8 |
61.7~88.0 |
|||||
HB |
127~651 |
80~638 |
80~683 |
90~646 |
83~663 |
81~646 |
|
HV |
83~976 |
80~937 |
80~996 |
84~1042 |
80~950 |
||
HS |
32.2~99.5 |
33.3~99.3 |
31.8~102.1 |
35.8~102.6 |
30.6~96.8 |
||
Hammered steel |
HB |
143~650 |
|||||
Cold work tool steel |
HRC |
20.4~67.1 |
19.8~68.2 |
20.7~68.2 |
22.6~70.2 |
||
HV |
80~898 |
80~935 |
100~941 |
82~1009 |
|||
Stainless steel |
HRB |
46.5~101.7 |
|||||
HB |
85~655 |
||||||
HV |
85~802 |
||||||
Gray cast iron |
HRC |
||||||
HB |
93~334 |
92~326 |
|||||
HV |
|||||||
Nodular cast iron |
HRC |
||||||
HB |
131~387 |
127~364 |
|||||
HV |
|||||||
Cast aluminum alloys |
HB |
19~164 |
23~210 |
32~168 |
|||
HRB |
23.8~84.6 |
22.7~85.0 |
23.8~85.5 |
||||
Brass(copper-zinc alloys) |
HB |
40~173 |
|||||
HRB |
13.5~95.3 |
||||||
Bronze (copper-aluminum/copper-tin alloys) |
HB |
60~290 |
|||||
Wrought copper alloys |
HB |
45~315 |
Non conventional impact devices |
DC(D)/DL |
D+15 |
C |
G |
E |
|
Impacting energy Mass of impact body |
11Mj 5.5g/7.2g |
11mJ 7.8g |
2.7mJ 3.0g |
90mJ 20.0g |
11mJ 5.5g |
|
Test tip Hardness Diameter of test tipMaterial of test tip |
1600HV 3mm Tungsten carbide |
1600HV 3mm Tungsten carbide |
1600HV 3mm Tungsten carbide |
1600HV 5mm Tungsten carbide |
5000HV 3mm synthetic diamond |
|
Impact device Diameter Impact device Length Impact device Weight |
20mm 86(147)/ 75mm 50g |
20mm 162mm 80g |
20mm 141mm 75g |
30mm 254mm 250g |
20mm 155mm 80g |
|
Max. hardness of workpiece |
940HV |
940HV |
1000HV |
650HB |
1200HV |
|
Mean roughness of workpiece surface of the Ra |
1.6μm |
1.6μm |
0.4μm |
6.3μm |
1.6μm |
|
Min. weight of sample Measure directly Need support firmly Need coupling tightly |
>5kg 2~5kg 0.05~2kg |
>5kg 2~5kg 0.05~2kg |
>1.5kg 0.5~1.5kg 0.02~0.5kg |
>15kg 5~15kg 0.5~5kg |
>5kg 2~5kg 0.05~2kg |
|
Min. thickness of sample coupling tightly Min.layer thickness for surface harden |
5mm ≥0.8mm |
5mm ≥0.8mm |
1mm ≥0.2mm |
10mm ≥1.2mm |
5mm ≥0.8mm |
|
Size of tip indentation |
||||||
Hardness 300HV |
Indentation diameter |
0.54mm |
0.54mm |
0.38mm |
1.03mm |
0.54mm |
Indentation depth |
24μm |
24μm |
12μm |
53μm |
24μm |
|
Hardness 600HV |
Indentation diameter |
0.54mm |
0.54mm |
0.32mm |
0.90mm |
0.54mm |
Indentation depth |
17μm |
17μm |
8μm |
41μm |
17μm |
|
Hardness 800HV |
Indentation diameter |
0.35mm |
0.35mm |
0.35mm |
– |
0.35mm |
Indentation depth |
10μm |
10μm |
7μm |
– |
10μm |
|
Available type of impact device |
D: General test DC: Hole or hollow-cylindrical test DL: Slender narrow groove or hole test |
D+15: groove or reentrant surface |
C: small, light, thin parts or surface of hardend layer |
G: large, thick, heavy or rough surface steel |
E: super high hardness material |
Type of Impact Device |
Distance of center of the two indentations |
Distance of center of the indentation to sample edge |
Not less than (mm) |
Not less than (mm) |
|
D、DC |
3 |
5 |
DL |
3 |
5 |
D+15 |
3 |
5 |
G |
4 |
8 |
E |
3 |
5 |
C |
2 |
4 |
Product detail pictures:
Related Product Guide:
As for aggressive rates, we believe that you will be searching far and wide for anything that can beat us. We can easily state with absolute certainty that for such good quality at such charges we are the lowest around for OEM/ODM Factory Dynamic Hardness Tester - The Impact Device of Hardness Tester – TMTeck , The product will supply to all over the world, such as: Mumbai, Eindhoven, Accra, With many years good service and development, we've a professional international trade sales team. Our products have exported to North America, Europe, Japan, Korea, Australia, New Zealand, Russia and other countries. Looking forward to build up a good and long term cooperation with you in coming future!
By Maud from Victoria - 2018.12.30 10:21
The customer service reprersentative explained very detailed, service attitude is very good, reply is very timely and comprehensive, a happy communication! We hope to have a opportunity to cooperate.
By June from Israel - 2018.10.31 10:02